In this paper, we report fabrication and investigation of ytterbium-doped phosphorsilicate fiber (P co-doped YDF) with high Yb content, low numerical aperture, and low background loss. The P co-doped YDF is fabricated by MCVD using the vapor sources of Yb, SiCl4, AlCl3, and POCl3, and by the gas-phase doping method. The optical properties of this P co-doped YDF are compared with Al co-doped and Al:P co-doped YDFs with low background losses. The minimum background loss of the P co-doped YDF in the spectral range from 1100 to 1380 nm is as low as ~3 dB/km. This is nearly independent of the Yb and P contents because soot deposition and collapsing conditions are properly optimized (i.e., the P co-doped YDF from a non-optimized process shows a few hundred dB/km). The excess loss induced by PD, for the P co-doped YDF, was dramatically reduced compared to both Al co-doped and Al:P co-doped YDFs. The optical slope efficiency of the P co-doped YDF is about 80%, depending on the pumping wavelength and fiber length. The fiber colors during pumping are blue for both the P co-doped and Al:P co-doped YDFs. Based on the results from a prolonged test, the output power of the P co-doped YDF is highly stable, with an initial degradation of 2-3%; which demonstrate improvement in PD resistivity with P incorporation into the glass, compared to the Al:P co-doped YDF with degradation above 6%.
Access to the requested content is limited to institutions that have purchased or subscribe to SPIE eBooks.
You are receiving this notice because your organization may not have SPIE eBooks access.*
*Shibboleth/Open Athens users─please
sign in
to access your institution's subscriptions.
To obtain this item, you may purchase the complete book in print or electronic format on
SPIE.org.
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.