The purpose of this research project is to improve the capability of the laser micromachinning process, so that any desired 3D surface can be produced by taking the 3D information from a CAD system and automatically generating the NC part programs. In addition, surface quality should be able to be controlled by specifying optimised parameters. This paper presents the algorithms and a software system, which processes 3D geometry in an STL file format from a CAD system and produces the NC part program to mill the surface using the Excimer laser ablation process. Simple structures are used to demonstrate the prototype system's part programming capabilities, and an actual surface is machined.
This paper presents the results of our investigations on the laser micromachining of structures in a dry film photoresist polymer (Dynachem, Laminar AX dry film) laminated on a copper clad Printed Circuit Board (PCB) and (100) Silicon wafer coated with Ti (15nm)/Cu (100 to 4000 nm) and copper seed layers. This study concentrated on investigating and comparing the effect of laser fluence (0.01 to 2 J/cm2) and number of shots (1 to 1000) on the etch characteristics of the Laminar AX dry film on both substrates. The other important aspects that were studied include the minimum required seed layer thickness for electroplating.The removal of the residual polymer layer at the end of the laser micromachining process and its effect on plating characteristics has been studied. The surface quality and roughness of the laser micromachined sites and their effect on the plated Nickel structures have also been investigated. The laser fluence and the number of shots used at this stage affected the conditions of the seed layer, which in turn influenced the plated film growth kinetics. The seed layers with thicknesses less than or equal to 0.8 µm were completely removed when high fluence (< around 1 J/cm2) was used. The seed layer surface after micromachining was characterised using Scanning Electron Microscopy (SEM), Xray photoelectron spectroscopy (XPS) and profilometer. High Aspect Ratio Structures (HARS) of Nickel were fabricated using the Laminar AX moulds. The highest aspect ratio achieved so far in this work is 6. The characteristics of these structures are discussed in detail.
Access to the requested content is limited to institutions that have purchased or subscribe to SPIE eBooks.
You are receiving this notice because your organization may not have SPIE eBooks access.*
*Shibboleth/Open Athens users─please
sign in
to access your institution's subscriptions.
To obtain this item, you may purchase the complete book in print or electronic format on
SPIE.org.
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.