Impact of rapid thermal annealing on dilute nitride (GaAsN) capped InAs/GaAs quantum dots exhibiting optical emission beyond ~1.5 µm

M. Biswas; A. Balgarkashi; S. Singh; N. Shinde; R. L. Makkar; A. Bhatnagar; Subhananda Chakrabarti

doi:10.1117/12.2237616

16 September 2016 Impact of rapid thermal annealing on dilute nitride (GaAsN)-capped InAs/GaAs quantum dots exhibiting optical emission beyond ~1.5 μm

M. Biswas, A. Balgarkashi, S. Singh, N. Shinde, R. L. Makkar, A. Bhatnagar, Subhananda Chakrabarti

Author Affiliations +

Proceedings Volume 9919, Nanophotonic Materials XIII; 991914 (2016) https://doi.org/10.1117/12.2237616
Event: SPIE Nanoscience + Engineering, 2016, San Diego, California, United States

Abstract

We report here self-assembled 2.6 ML InAs QDs capped with GaAsN0.021 on GaAs (001) substrate grown under high arsenic overpressure and high power by solid source molecular beam epitaxy. With variation in GaAsN_0.021 layer thickness, InAs/GaAs QDs were studied by photoluminescence (PL) spectroscopy. It was found that with InAs dot density of 3 ×10¹⁰ cm^-2 and 4 nm GaAsN capping layer, emission wavelength was possible to extend beyond 1.5 μm at 300K. Rapid thermal annealing was carried out in nitrogen ambient for 30 sec at temperatures ranging from 700°C to 800°C and a continuous blue-shift for the nitride-capped QDs was observed at 19 K PL spectra, and the sample annealed at 800°C exhibited highest intensity with narrowest full width at half maximum (FWHM). Both the as-grown and annealed samples exhibited asymmetric PL behavior in low energy region at low temperature, associated to the N-related states or cluster of N atoms. The peak emission wavelength at the annealing temperature domain of 750-800°C was remained constant, attributed to no In/Ga diffusion at the interface between the dot and the barrier. Hence, the InAs/GaAs dots capped with 4-nm GaAsN_0.021 layer could be implemented in lasers in the temporal range of 750-800°C.

Citation Download Citation

M. Biswas, A. Balgarkashi, S. Singh, N. Shinde, R. L. Makkar, A. Bhatnagar, and Subhananda Chakrabarti "Impact of rapid thermal annealing on dilute nitride (GaAsN)-capped InAs/GaAs quantum dots exhibiting optical emission beyond ~1.5 μm", Proc. SPIE 9919, Nanophotonic Materials XIII, 991914 (16 September 2016); https://doi.org/10.1117/12.2237616

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available