CO2 laser welding of aluminum alloys at high speeds up to 20 m/min

Kunimitsu Takahashi; Mikio Kumagai; Seiji Katayama; Akira Matsunawa

doi:10.1117/12.497789

3 March 2003 CO₂ laser welding of aluminum alloys at high speeds up to 20 m/min

Kunimitsu Takahashi, Mikio Kumagai, Seiji Katayama, Akira Matsunawa

Proceedings Volume 4831, First International Symposium on High-Power Laser Macroprocessing; (2003) https://doi.org/10.1117/12.497789
Event: LAMP 2002: International Congress on Laser Advanced Materials Processing, 2002, Osaka, Japan

Abstract

CO₂ laser welding of thin aluminum sheets was performed at welding speeds of up to 20 m/min to investigate the weldability, weld pool dynamics and mechanical properties of the weld bead of aluminum alloys. High-speed camera observation of weld areas showed that the thickness of the keyhole-front-face decreased to 100 μm under high-speed welding conditions and the weld pool became unstable. The focal length was optimized to increase the spot power density and thereby easily melt the aluminum sheets. Using a 76-mm focal length lens, which corresponds to 11 MW/cm² power density, we obtained a keyhole mode weld bead with a depth of 1.3 mm at 20 m/min welding speed at 2 kW laser power. It was also possible to reduce the heat affected zone (HAZ) width to only 1.6 mm when the welding speed was 20 m/min. The HAZ width decreased as welding speed was increased. The tensile strength test of A6N01 weld beads showed that the fracture strength increased as the welding speed was increased up to 16 m/min, probably because the soft region of weld specimens was decreased. On the other hand, solidification cracks formed in the weld bead center at higher speeds, resulting in decreased strength.

Citation Download Citation

Kunimitsu Takahashi, Mikio Kumagai, Seiji Katayama, and Akira Matsunawa "CO₂ laser welding of aluminum alloys at high speeds up to 20 m/min", Proc. SPIE 4831, First International Symposium on High-Power Laser Macroprocessing, (3 March 2003); https://doi.org/10.1117/12.497789

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available

Members: $17.00

Non-members: $21.00 ADD TO CART

PROCEEDINGS
6 PAGES

DOWNLOAD PAPER SAVE TO MY LIBRARY

GET CITATION

RIGHTS & PERMISSIONS

Get copyright permission Get copyright permission on Copyright Marketplace

KEYWORDS

Laser welding

Aluminum

Carbon dioxide lasers

High speed cameras

Solids

Argon

Metals

Show All Keywords

Keywords/Phrases

Search In:

Publication Years